Room and high-temperature tensile properties of austenitic stainless steel 321 fabricated by wire arc additive manufacturing

초록

SS 321 is a potential structural alloy for elevated temperature applications. In this work, austenitic stainless steel 321 (SS 321) was successfully fabricated via wire arc additive manufacturing (WAAM). Microstructural analysis of the wrought SS 321 revealed the presence of equiaxed grains. In contrast, the WAAM 321 wall structure comprised equiaxed, columnar, and elongated dendrites with ferrite fractions ranging from 3.6 to 5.9 FN. Further, the WAAM 321 exhibited better hardness than the wrought alloy. WAAM 321 samples exhibited excellent tensile properties compared to the SS 321 wrought alloy, while the tensile strength and ductility decreased considerably from room temperature (RT) to elevated temperatures (900 degrees C). The average tensile strength of SS 321 at 900 degrees C was 108 +/- 6 MPa, and the WAAM 321 samples showed higher strength (similar to 135 +/- 7 MPa). The decrease in tensile strength is attributed to the activation of a multi-slip system, resulting in a lower resistance to dislocation motion at elevated temperatures. Also, serrated yielding was observed at 600 degrees C due to dynamic strain aging. The fractured surface characteristics align with the ductility trend. This research highlights the role of WAAM in manufacturing high-performing structures for elevated temperature environments.

키워드