알루민산칼슘 시멘트를 사용한 모르타르의 수화도에 따른 철근 부식 특성

초록

The present study concerns the resistance of calcium aluminate cement (CAC) to steel corrosion. The corrosion behavior of steel, chloride binding/buffering and chloride transport were evaluated in order to predict the risk of steel corrosion. The CAC mortar exhibited no corrosion on steel, irrespective of the curing temperature and CAC types, whereas ordinary Portland cement (OPC) showed a severe corrosion on the steel surface. The chloride binding capacity of CAC found to be was lower than that of OPC, yet buffering capacity against pH decrease was found to be significantly higher in the CAC paste. Furthermore, chloride ingress at all depths was found to be reduced in CAC, thereby reducing the risk of corrosion.