Corrosion resistance performance of arc thermal sprayed Al and Al/epoxy dual metal polymeric coating in 3.5 wt.% NaCl-contaminated concrete pore solution

초록

Corrosion of the steel rebar in coastal environment caused huge economical loss of the globe. Therefore, coating on the steel rebar being used to mitigate the corrosion. In the present study, we have applied epoxy coating on arc thermal sprayed Al coating (a dual metal/polymeric coating) vis-a-vis compared with as coated one (Al coating). The corrosion studies were performed in simulated concrete pore solution with 3.5 wt. % NaCl solution. The morphology of the dual epoxy/Al coating is smooth while Al coating shows rankle and defects. Due to defects, Al coating is susceptible to corrosion while dual epoxy/Al coating has performed excellent compared to as coated one at extended period of immersion.